Study on Preparation and Performance of POE/SBS/C5 Composite Modified Asphalt
1. School of Food and Biological Engineering, Hubei University of Technology, Wuhan 430068, China;
2. School of Mechanical Engineering, Wuhan Vocational College of Software and Engineering, Wuhan 430205, China;
3. Hubei Provincial Key Laboratory of Light Industrial Materials, Hubei University of Technology, Wuhan 430068, China
Abstract The construction of a "sponge city" requires asphalt to have excellent permeability and mechanical properties. At present, styrene-butadiene-styrene block polymer (SBS) modified asphalt is predominant, but it has the disadvantages of high cost and low stability due to the double bond in the chain. In this paper, polyethylene-octene copolymer (POE), SBS, petroleum resin (C5) and sulfur were used as composite modifiers. The influence of POE to SBS ratio, the content of C5 and sulfur in the modifier on the softening point, ductility, penetration and viscosity of the modified asphalt were studied. The results showed that the comprehensive performance of modified asphalt was preferred when the ratio of POE to SBS was 0.8:9.2 with a total content of 65% in the modifier and the content of C5 petroleum resin and sulfur in the modifier was 5% and 4% respectively. The softening point of the modified asphalt reached 91.06 ℃, ductility reached 44.3 cm, penetration degree reached 35.9 (0.1 mm), and viscosity reached 30 184 Pa·s. The obtained modified asphalt mixture had dynamic stability of 11 613 times/mm, porosity of 24.2% and viscosity toughness of 21.841 N·m, it meets the requirements of high-viscosity modified asphalt and had good high temperature stability and anti-rutting ability.
ZHOU Wenpei1,DENG Ling2,YU Peng3 et al. Study on Preparation and Performance of POE/SBS/C5 Composite Modified Asphalt[J]. 化学反应工程与工艺, 2020, 36(3): 283-288.
ZHOU Wenpei1,DENG Ling2,YU Peng3 et al. Study on Preparation and Performance of POE/SBS/C5 Composite Modified Asphalt[J]. Chemical Reaction Engineering and Technology, 2020, 36(3): 283-288.