Effect of Precipitants on the Performance of ZnCr Oxide Catalysts in the Isobutanol Synthesis
State Key Laboratory of Green Chemical Engineering and Industrial Catalysis, Shanghai Research Institute of Petrochemical Technology, SINOPEC, Shanghai 201208, China
Abstract In order to develop highly selective and stable catalysts for the synthesis of isobutanol, different precipitants were selected and a series of ZnCr based oxide catalysts were prepared by co-precipitation method. The texture parameters, structure and reduction properties of the catalysts were characterized by N2 adsorption-desorption technique, X-ray diffraction (XRD) and temperature-programmed reduction (H2-TPR). The catalytic performance of CO hydrogenation to isobutanol was studied. The characterization results indicate that when weak base is used as the precipitant, the non-stoicheiometric spinel ZnxCr2/3(1-x)O is formed, which has large specific surface area, and exhibits good dispersion and reducibility. When strong base is used as the precipitant, the specific surface area of the prepared catalyst is small, the reducibility is poor, and the phase separation is observed. It was found that the ZnCr catalyst precipitated by (NH4)2CO3 shows the best catalytic performance. ZnCr-(NH4)2CO3 catalyst could achieve 15.3% CO conversion, 90.3% alcohols selectivity, and 33.5% isobutanol selectivity at the condition of 390 oC, 10 000 h-1 and 12 MPa.
Zhou Haibo,Liu Su,Wang Yangdong. Effect of Precipitants on the Performance of ZnCr Oxide Catalysts in the Isobutanol Synthesis[J]. 化学反应工程与工艺, 2017, 33(3): 243-248.
Zhou Haibo,Liu Su,Wang Yangdong. Effect of Precipitants on the Performance of ZnCr Oxide Catalysts in the Isobutanol Synthesis[J]. 化学反应工程与工艺, 2017, 33(3): 243-248.